SLA KS168C is a new generation of stereolithography resin specially developed for the production of investment casting patterns after long-term innovation by Kings R&D team.
This transparent resin was created to improve the repeatability and quality of 3D-printed casting patterns.
Patterns created with this SLA material have higher precision and toughness, and have good dimensional stability, In addition, it has excellent processability, making it an ideal material for investment casting.
Advantages:
- Fast to build and easy to finish
- Excellent humidity and moisture resistance
- Excellent processability
- High precision and toughness
- Good dimensional stability
Ideal Applications:
- Patterns for investment casting
- Transparent display models
- Conceptual prototypes
- Tough functional prototypes
Technical Datasheet:
Optical Properties | Optical Properties |
Appearance
| transparent | Dp | 0.15-0.19 mm |
Viscosity
| 340-470cps/24.5℃ | Building layer thickness | 0.15-0.19 mm |
Density
| 1.095-1.11g/cm3 @ 25 ℃ |
|
|
Mechanical Properties | UV Postcure |
MEASUREMENT | TEST METHOD | VALUE |
Hardness, Shore D
| ASTM D 2240 | 80-84D |
Flexural modulus, Mpa | ASTM D 790 | 1850-2550 |
Flexural strength, Mpa | ASTM D 790 | 50-69 |
Tensile modulus, MPa | ASTM D 638 | 1700-2380 |
Tensile strength, MPa | ASTM D 638 | 47-55 |
Elongation at break | ASTM D 638 | 4.2-9% |
Impact strength, notched Izod, J/m | ASTM D 256 | 42-49 |
Heat deflection temperature, ℃ | ASTM D 648 @66PSI | 48-60 |
Glass transition, Tg，℃ | DMA, E''peak | 60-70 |
Density, g/cm3 | 1.156-1.157 |
If you want to know more information, Welcome Contact Kings Professional Sales.